ELASTOFALT SPRAYKOTE 90 | Sprayed waterproofing for the bridge
Elastic bituminous emulsion waterproofing for concrete floors and screeds
Basement floor waterproofing
Floor waterproofing under screed
Foundation waterproofing
Elastofalt Spraykote 90 | Liquid bitumen-polymer two-component emulsion.
Key features and benefits of Elastofalt Spraykote 90 :
-
application of material in the form of a homogeneous highly elastic membrane;
-
applied to the surface of any geometric shape;
-
high performance: up to 2000 sq.m. for a shift;
-
applied without heating, environmentally friendly;
- surface irregularities do not affect the quality of the formed membrane.
Application of " Elastofalt Spraykote 90 ":
-
waterproofing of foundations, basement walls, retaining walls;
-
waterproofing of roofs, terraces, exploited and green roofs;
-
waterproofing of parking lots, bridge supports, tunnels, underpasses, metro stations;
-
waterproofing and protection against penetration of aggressive substances into the ground from collector networks and garbage storages;
-
horizontal waterproofing for all mineral substrates;
-
under asphalt, concrete floor, cement screed;
-
protection against moisture of all types of underground structures;
-
bridge waterproofing;
-
flyover waterproofing;
-
waterproofing of overpasses;
-
waterproofing of balconies and open terraces.
Waterproofing overpass
Physical and mechanical characteristics of the membrane Elastofalt Spraykote 90
|
Bulk weight of the emulsion |
1020 kg/m 3
|
|
Tensile strength at 0 ºС |
130 kg/ cm2
|
|
Tensile strength after ultraviolet irradiation for 1000 hours |
120 kg/ cm2
|
|
Tensile strength after immersion in water for 720 hours at 50 ºС |
126 kg/ cm2
|
|
Conditional strength at break |
0.9 MPa
|
|
Elongation at t 20 ºС |
1200%
|
|
Flexibility at low temperature |
30 ºС
|
|
Return to original position at 1000% stretch |
over 85%
|
|
Water resistance, 4 mm |
0.35 MPa
|
|
Heat resistance, not less |
100 ºС
|
|
Adhesion strength to the base |
0.86 MPa
|
Application technology Elastofalt Spraykote 90
-
Liquid polymer-bitumen emulsion and coagulant are applied simultaneously using a double spray nozzle, on the prepared base;
-
When these two components are mixed, a coagulation process occurs;
-
As soon as the constituents reach the surface, a continuous and seamless membrane is formed, which is initially insensitive to water;
-
The stabilization process depends on the thickness of the membrane, humidity and air temperature;
-
Freezing does not disrupt the stabilization process if the coating is not subjected to mechanical stress;
-
Consumption: 3-7 kg/sq.m.
Elastic waterproofing for the bridge